TerraPro ® T15-10-15-NAT

TerraPro ® Talc Series

Filled Talc Polypropylene

Technical Datasheet

Product Description

10% talc filled Polypropylene copolymer for injection molding applications, offering good stiffness and good dimensional stability.

Features:

Good processability

Good stiffness/impact balance

Compatible with PP and olefinic TPE's

General

Availability

North America

Material Status

Commercial: Active

Filler / Reinforcement

Talc, 10% Filler by Weight

Processing Method

Injection Molding

Key Properties

Good Processability

Good Impact Resistance

Copolymer

Good Dimensional Stability

Good Stiffness

Key Applications

Consumer Applications

Automotive

Industrial

Physical

Value (SI)

Test Method

Density / Specific Gravity

0.970 g/cm3

ASTM D792

Melt Mass-Flow Rate, 230°C/2.16 kg load

15 g/10min

ASTM D1238

Molding Shrinkage - Flow

0.9 to 1.2 %

ASTM D955

Mechanical

Value (SI)

Test Method

Tensile Strength (Yield)

19.4 MPa

ASTM D638

Flexural Modulus - 1% Tangent

1310 MPa

ASTM D790

Tensile Elongation (Break)

80 %

ASTM D638

Impact

Value (SI)

Test Method

Notched Izod Impact (23°C)

130 j/m

ASTM D256

Gardner Impact (23°C)

18.1 J

ASTM D5420

Hardness

Value

Test Method

Durometer Hardness

ASTM D2240

Thermal

Value (SI)

Test Method

Deflection Temperature Under Load

0.45 MPa, Unannealed

110 °C

ASTM D648

Polymerixx Grade

Nex-Pro AKZT15-10-25 NAT

Polypropylene

Value

Copolymer

✔

The above test results are obtained from laboratory injection molded ISO samples and cannot be used directly to determine end-use or design specification. The customer should determine the suitability to his/her application through their internal testing procedure. Datasheet values represent a statistical average or product properties and they may change with incr. data points.