TerraPro ® T30-20-01

TerraPro ® Caco3 Series

TerraPro ® Talc Series

TerraPro ® TPO

Filled Talc Polypropylene

Technical Datasheet

Product Description

20% Talc Filled HOMOPOLYMER POLYPROPYLENE Meets UL 94 HB.

Features:

Good processability

High Stiffness

Compatible with PP and olefinic TPE's

General

Availability

North America

Material Status

Commercial: Active

Filler / Reinforcement

Talc, 20% Filler by Weight

Key Properties

Good Processability

High Stiffness

Homopolymer

Key Applications

Consumer Applications

Automotive

Industrial

Physical

Value (SI)

Test Method

Density / Specific Gravity

1.05 g/cm3

ASTM D792

Melt Mass-Flow Rate, 230°C/2.16 kg load

30 g/10min

ASTM D1238

Molding Shrinkage - Flow

0.40 %

ASTM D955

Mechanical

Value (SI)

Test Method

Tensile Strength (Yield)

31.0 MPa

ASTM D638

Flexural Modulus - 1% Tangent

2070 MPa

ASTM D790

Impact

Value (SI)

Test Method

Notched Izod Impact (23°C)

32 j/m

ASTM D256

Thermal

Value (SI)

Test Method

Deflection Temperature Under Load

1.8 MPa, Unannealed

127 °C

ASTM D648

Flammability

Value

Test Method

Flame Rating

UL 94

Polypropylene

Value

Homopolymer

✔

Polymerixx Grade

Nex-Pro AKZT30-20-01

The above test results are obtained from laboratory injection molded ISO samples and cannot be used directly to determine end-use or design specification. The customer should determine the suitability to his/her application through their internal testing procedure. Datasheet values represent a statistical average or product properties and they may change with incr. data points.