40 Shore D TPE for injection molding and extrusion applications, offering high tensile strength and toughness, adhesion (overmolding or coextrusion) to Polypropylene, and good weatherabilty.
| Melt Temperature: | 200-220 °C |
| Screw Speed: | 50 to 200 rpm |
| Shrinkage: | 0.012 – 0.018 in/int |
| Back Pressure: | 50-100 psi (0.345-0.689 MPa) |
| Screw L/D Ratio: | 16:1.0 to 20:1.0 |
| Screw Compression Ratio: | 2.0:1.0 to 2.5:1.0 |
|
|||||
| C: | 170-200 | 180-220 | 180-210 | 190-220 | 15-50 |
| F: | 338-392 | 356-428 | 356-410 | 374-428 | 59-122 |
| Melt Temperature: | 190-200 °C |
| Die Temperature: | 190-210 °C (347-428 °F) |
| Back Pressure: | 5.0-20 MPa (725-2900 psi) |
| Screw Speed: | 100 to 200 rpm |
|
|||||
| C: | 160-180 | 170-190 | 180-200 | 190-210 | 190-210 |
| F: | 320-356 | 338-374 | 356-392 | 374-410 | 374-410 |
The above test results are obtained from laboratory injection molded ISO samples and cannot be used directly to determine end-use or design specification. The customer should determine the suitability to his/her application through their internal testing procedure. Datasheet values represent a statistical average or product properties and they may change with incr. data points.