90 Shore A TPE (Styrenic Block Copolymer based) for injection molding and 69+ extrusion applications, offering soft and tactile feel, good wet and dry grip, and adhesion (overmolding or coextrusion) to Polypropylene.
Melt Temperature: | 200-220 °C |
Screw Speed: | 50 to 200 rpm |
Injecjon Rate: | Fast |
Back Pressure: | 50-100 psi (0.345-0.689 MPa) |
Cushion | 0.125-0.25 in (3.18-6.35 mm) |
Screw L/D Ratio: | 16:1.0 to 20:1.0 |
Screw Compression Ratio: | 2.0:1.0 to 2.5:1.0 |
C: | 170-200 | 180-210 | 190-220 | 200-230 | 10-50 |
F: | 338-392 | 356-410 | 374-428 | 392-446 | 50-122 |
Drying Temperature: | 70 °C (160 °F) |
Drying Time: | 3.0 hr Melt Temperature: 190-200 |
Melt Temperature: | 190-200 °C |
Die Temperature: | 204 °C (400 °F) |
Back Pressure: | 5.0-20 MPa (725-2900 psi) |
Screw Speed: | 100 to 200 rpm |
C: | 160-180 | 170-190 | 180-200 | 190-210 | 190-210 |
F: | 320-356 | 338-374 | 356-392 | 374-410 | 374-410 |
The above test results are obtained from laboratory injection molded ISO samples and cannot be used directly to determine end-use or design specification. The customer should determine the suitability to his/her application through their internal testing procedure. Datasheet values represent a statistical average or product properties and they may change with incr. data points.