TerraFlex® S7165A NAT

TPE

TerraFlex® S7165A NAT
SBS for injection molding and extrusion
Technical Datasheet
General
Availability
North America
Europe
Latin America
Asia/China
Africa
Appearance
Natural Color
Processing Method
Injection Molding
Extrusion
Properties
Easy Processing
Easy Processing
high Flow
high Flow
Good Adhesion
Good Adhesion
Good Compression Set
Good Compression Set
Key Applications
Consumer Applications
Consumer Applications
Automotive
Automotive
Appliance Components
Appliance Components
Sporting Goods
Sporting Goods
Household
Household
Physical
Value (SI)
Test Method
Density/Specific Gravity
0.95 g/cm3
ISO 1183, ASTM D1238
Melt Mass-Flow Rate, 190°C/2.16 kg load
15 g/10min
ASTM D1238
hardness
Value (SI)
Test Method
Durometer Hardness
Shore A, 10 Sec, Injection Molded
65
ISO 868, ASTM D2240
Shore A, 10 Sec, Exruded
62
ISO 868, ASTM D2240
Elastomers
Value (English)
Value (SI)
Test Method
Tensile Strength at Break
725 psi
5 MPa
ISO 37, ASTM D412
Elongation at Break
450 %
450 %
ISO 37, ASTM D412
100% Modulus
260 psi
1.79 MPa
ISO 37, ASTM D412
Tear Strength
150 lbs/in
23.6 kN/m
ISO 34-1, ASTM D624
Compression Set
Value (English)
Value (SI)
Test Method
72h/23 °C (73 °F)
22 %
22 %
ISO 815, D395B
Service Temperature
Value (SI)
Brittleness Point
-50 °C
Dynamic Service Temperature
50 °C
Environmental Resistance
Ozone
Alcohol
Weak Acid
Water
Detergent
Rheology
Value (SI)
Test Method
Viscosity @ 243 sec-1/200°C
165 Pa-sec
ASTM D1238

Processing Guide


Injection Molding

Melt Temperature: 200-220 °C
Screw Speed: 50 to 200 rpm
Injecjon Rate: Fast
Back Pressure: 50-100 psi (0.345-0.689 MPa)
Cushion 0.125-0.25 in (3.18-6.35 mm)
Screw L/D Ratio: 16:1.0 to 20:1.0
Screw Compression Ratio: 2.0:1.0 to 2.5:1.0
C: 170-200 180-210 190-220 200-230 10-50
F: 338-392 356-410 374-428 392-446 50-122

Extrusion

Drying Temperature: 82 °C (180 °F)
Drying Time: 3.0 hr
Melt Temperature: 190-200 °C
Die Temperature: 204 °C (400 °F)
Back Pressure: 5.0-20 MPa (725-2900 psi)
Screw Speed: 50 to 200 rpm
C: 170-190 160-180 180-200 190-210 190-210
F: 338-374 320-356 356-392 374-410 374-410
  • It is not necessary to predry this material.
  • In the event of moisture accumulation or evidence of splay, the material can be dried for 2-3 hours at 150-160F (65-70C).
  • For more information please contact us via customerservice@compounding.us


The above test results are obtained from laboratory injection molded ISO samples and cannot be used directly to determine end-use or design specification. The customer should determine the suitability to his/her application through their internal testing procedure. Datasheet values represent a statistical average or product properties and they may change with incr. data points.