TerraPrene ® V2165A-NAT
Enhanced Thermoplastic Vulcanizate TPV, based on EPDM and Polypropylene, with improved UV resistance and surface aesthetics (for extrusion)
Technical Datasheet
Product Description
65 Shore A Thermoplastic Vulcanizate for injection molding and extrusion applications, offering excellent flex fatigue, very good temperature and fluid resistance, very good compression set properties, low gloss and compatibility with polyolefins.
General
Key Properties
Key Applications
Tensile Stress 100% Strain
419 psi
2.89 MPa
ISO 37, ASTM D412
Tensile Strength at Break
990 psi
6.83 MPa
ISO 37, ASTM D412
Tensile Elongation at Break
430 %
430 %
ISO 37, ASTM D412
Tear Strength
136.7 lbs/in
24 kN/m
ISO 34-1, ASTM D624
Change in Tensile Strength in Air - Across Flow 150°C (302°F) , 168 h
-12 %
ISO 1817, ASTM D573
Change in Ultimate Elongation in Air - Across Flow 150°C (302°F) , 168 hr
-0.5 %
ISO 188, ASTM D412
Change in Durometer Hardness in Air (Shore A, 150°C, 168 hr)
Change in Volume (125°C, 70 hr, in IRM 903 Oil)
Injection Molding
| Melt Temperature: |
200-220 °C |
| Screw Speed: |
50 to 200 rpm |
| Injection Rate: |
Fast |
| Back Pressure: |
50-100 psi (0.345-0.689 MPa) |
| Cushion: |
0.125-0.25 in (3.18-6.35 mm) |
| Screw L/D Ratio: |
16:1.0 to 20:1.0 |
| Screw Compression Ratio: |
2.0:1.0 to 2.5:1.0 |
|
|
|
| C: |
170-200
|
180-210
|
190-220
|
200-230
|
10-50
|
| F: |
338-392
|
356-410
|
374-428
|
392-446
|
50-122
|
Extrusion
| Drying Temperature: |
82 °C (180 °F) |
| Drying Time: |
3.0 hr |
| Melt Temperature: |
190-200 °C |
| Die Temperature: |
204 °C (400 °F) |
| Back Pressure: |
5.0-20 MPa (725-2900 psi) |
| Screw Speed: |
50 to 200 rpm |
|
|
|
| C: |
160-180
|
170-190
|
180-200
|
190-210
|
190-210
|
| F: |
320-356
|
338-374
|
356-392
|
374-410
|
374-410
|
-
It is recommended to pre-dry this material. In the event of moisture accumulation or evidence of splay, the material can be dried for 2-3 hours at 70-80°C.
-
For more information please contact us via customerservice@compounding.us
The above test results are obtained from laboratory injection molded ISO samples and cannot be used directly to determine end-use or design specification. The customer should determine the suitability to his/her application through their internal testing procedure. Datasheet values represent a statistical average or product properties and they may change with incr. data points.